对国产汽车所用210种涂层试样进行了湿热带大气环境自然曝晒试验及人工加速老化试验。
Natural exposing tests in humid tropics atmosphere environment and accelerated ageing tests for 210 coat test samples of domestic automotives are carried out.
阐述了美国QUV老化机和氙灯老化机在人工加速老化试验中的性能特点,以及各自的适用领域。
Characteristics of America QUV aging machine and Xenon lamp aging applied in artificial accelerated experiments are described. Their application fields are given also.
以聚丙烯长丝为对象,采用不同紫外线辐射强度的人工加速老化试验对其光氧老化过程进行研究。
The photo-oxidation ageing process of polypropylene filaments was studied by artificial accelerated ageing test using different intensities of UV irradiation.
采用盐雾和紫外-冷凝室内人工加速老化循环试验的方法,对聚氨酯和丙烯酸两种典型的船壳涂料进行人工加速老化试验。
The degradation of two coatings systems based on polyurethane and acrylic were studied by exposed in UV-condensation chamber and salt-fog chamber alternately.
经人工加速老化和扣棚自然老化试验证明,用该专用料吹制的棚膜,其使用寿命可达1.5~2年,比普通膜寿命长3~4倍。
The experiment results of the artificial accelerated weathering and the naturally weathering confirm that the using life of this filmwillbe 1.5~ 2 years, which is 3~4 times longer than common films.
为此,采用室内人工加速试验方法,研究了石油沥青涂层的老化过程和规律。
The ageing process and regularity of the asphalt coating have been studied with indoor artificial accelerated ageing test.
通过FTIR、失重分析以及氢过氧化物分析表征人工加速耐老化检测中复合涂层光降解变化过程。
The process of photochemical degradation was assessed by Fourier Transform infra-red (FTIR) spectroscopy, weight loss and hydroperoxide analysis following artificial aging.
人工加速试验表明,6 911型光稳定剂与BW10ld和944相比,具有更为优异的长期防老化性能。
Artificial weathering test shows that 6911 has better long term anti aging performances than that of BW 10ld and 944.
采用室内贮存试验、人工加速湿热老化试验和红外光谱法研究了硬质聚氨酯泡沫塑料在室内贮存条件下的老化机理。
The aging mechanism of rigid polyurethane foams at indoor storage conditions was investigated with indoor storage tests, accelerated hygrothermal aging tests and IR spectra.
采用室内贮存试验、人工加速湿热老化试验和红外光谱法研究了硬质聚氨酯泡沫塑料在室内贮存条件下的老化机理。
The aging mechanism of rigid polyurethane foams at indoor storage conditions was investigated with indoor storage tests, accelerated hygrothermal aging tests and IR spectra.