指出欠烧或过烧菱苦土的采用是造成氯氧镁水泥硬化体胀裂的根本原因。
The result shows that the cause of fracturing is under-burning or over-burning of magnesia.
指出欠烧或过烧菱苦土的采用是造成氯氧镁水泥硬化体胀裂的根本原因。
Research on the composite magnesia cement of the caustic dolomite and the calcined magnesite;
当一个铝铆钉的镦头形成在较软的材料一边时，必需在铆钉镦头下使用垫片以防止较软材料胀裂。
When an aluminum rivet is upset against a softer material, a washer must be used under the upset head to prevent eruption of the softer material.
研究了混凝土保护层胀裂时及胀裂前锈蚀对无横向约束光圆钢筋混凝土试件粘结性能的影响机理。
The effect of corrosion on the bond between concrete and plain bar reinforcement without stirrups is studied during cover cracking and before cover cracking.
现在，我已经80多岁了，但是每当我回想起我爸当时的面部表情，我就感到我的心仍然在膨胀着，像是要胀裂一样。
I'm now in my 80s, but whenever I think of that look on Dad's face, my heart still feels as if it will swell up and burst.
通过全面检测和分析，指出混凝土骨料中含有的方镁石发生水化反应所引起的体积膨胀，是混凝土构件胀裂的根本原因。
Through some macro and micro inspections, the cause is found out of the volume expansion due to the hydration of magnesia in concrete aggregates.
根据有限元分析的结果，对混凝土保护层锈蚀胀裂破坏的弹性力学模型进行修正，建立了混凝土保护层锈蚀胀裂时钢筋锈蚀量的计算模型。
According the result of ANSYS analysis, a new model based elasticity mechanics is developed for calculating the corrosion loss that need for concrete cover cracking.
分析了影响混凝土保护层胀裂时钢筋锈蚀深度的各个因素，包括混凝土水泥石毛细孔的体积、混凝土保护层的厚度、钢筋直径和铁锈膨胀率。
The factors influencing the corrosion depth including the porous volume of concrete, thickness of concrete cover, diameter of rebar and the corrosion expansion rate are analyzed.
利用有限元软件ANSYS建立考虑箍筋间距、直径变化的钢筋混凝土构件锈胀裂分析模型，研究箍筋对纵筋锈蚀导致钢筋混凝土构件保护层胀裂的影响。
Considering the change of the spacing and diameter of stirrups, a corrosion-induced cracking module for concrete members is built by ANSYS.
利用有限元软件ANSYS建立考虑箍筋间距、直径变化的钢筋混凝土构件锈胀裂分析模型，研究箍筋对纵筋锈蚀导致钢筋混凝土构件保护层胀裂的影响。
Considering the change of the spacing and diameter of stirrups, a corrosion-induced cracking module for concrete members is built by ANSYS.