结果表明，该膜层的成分、形貌及结构与常规氧化膜有很大的区别，是一种新型铝氧化膜。
The results show that the film, greatly different from conventional oxide films in composition, morphology and structure, is a novel aluminum oxide film.
微弧氧化陶瓷层的耐蚀性优于阳极氧化和铬化处理膜层的耐蚀性。
The corrosion resistance of micro arc oxidation ceramic coating is better than the corrosion resistance of chromate and anode coating.
研究氧化时间对MB8镁合金氧化膜致密度、厚度和耐蚀性的影响，分析不同氧化时间膜层表面微观形貌、成分和结构的变化。
The effects of oxidation time on the density, thickness and corrosion resistance of the micro-arc oxidation coatings of MB8 magnesium alloy were investigated.
用扫描电镜（SEM）观察了氧化层的表面形貌，X射线衍射仪（XRD）分析了氧化膜层的相组成。
The oxidation surface morphology and the phases of the oxide scale were analyzed by using SEM and XRD.
阳极氧化加复合的较高温度的热氧化将得到粗糙、并分布着许多凹坑的转化膜层。
Anodizing with thermal oxidizing at higher temperature will get rough films with a many hollow.
在相同氧化电压条件下，膜层的综合性能以采用三角波形氧化最为优良，交流氧化次之，直流氧化最差。
At the same oxidation voltage, the film's corrosion resistance prepaved by triangle wave oxidation is the best, followed by AC oxidation, DC oxidation is the worst.
电解液浓度，氧化电压和氧化时间等参数，对膜层的形貌都有不同程度的影响。
The parameters such as the electrolyte concentration, oxidation voltage and oxidation time reveal different impacts on the morphology of the coatings.
将超声波应用于铝的阳极氧化处理，研究了超声波对阳极氧化特性曲线、电解工艺参数和膜层形貌的影响。
The ultrasonic technics was applied to anode oxidation of aluminum. The influences of ultrasonic on anode oxidation curves, electrolytic process parameters and oxide film's morphology were studied.
利用阴极等离子体液相沉积技术实现了在不锈钢表面制备氧化铝膜层，研究了氩气焙烧处理对膜层的结构、组成、形貌和抗高温氧化性能的影响。
The effects of the Ar calcination on the structure, phase composition, morphology and anti-high temperature oxidation property of the ceramic coatings were studied.
结果表明：阳极氧化膜因内外表面受到电解液的腐蚀程度不同而表现为氧化膜的硬度自膜层表面到基体逐渐升高。
The results showed that the hardness of oxide films increased from the surface to the substrate, because electrolyte corrosion between the internal and external surfaces was different.
固溶工艺的改变对阳极氧化膜的厚度均匀性无显著影响，氧化膜自身的成分结构决定了其膜层厚度的均匀性。
The change of heat treatment had no obvious effect on the uniformity of thickness, which was detected by the composition structure of the films.
本发明的镀氧化锌膜层的玻璃是由玻璃和镀在玻璃表面的氧化锌膜层组成。
A glass with plated zinc oxide film layer consists of glass and zinc oxide film coated onto the surface of glass.
研究结果发现：两种钛合金经过氧化后，均在表面生成一层氧化膜；
The results show that: oxide scales are found on the surface of this two Ti-alloys;
研究结果发现：两种钛合金经过氧化后，均在表面生成一层氧化膜；
The results show that: oxide scales are found on the surface of this two Ti-alloys;