通过自制的冲击腐蚀磨损试验机,施加不同极化电位对高锰钢在矿浆介质中的冲击腐蚀磨损行为进行了试验研究。
Effect of polarization potential on the corrosion-wear behavior of high manganese steel in ore slurry was investigated by a self-made impact corrosive-wear tester.
在改进的MLD - 10型冲击腐蚀磨损试验机上,对不同成分的低碳高合金钢的冲击腐蚀磨损性能进行了测试。
LCHA with several variations of composition were tested with a modified MLD-10 wear tester to investigate their behavior under corrosive impact abrasion.
结果表明,在相同试验条件下低碳高合金钢的冲击腐蚀磨损性能要优于高锰钢的。
The results show that the resistance of low carbon high alloy steel is better than that of the high manganese steel under the same test condition.
在改进的MLD - 10型冲击腐蚀磨损试验机上,选择三种不同的冲击功,对以锰代镍的低碳高合金钢的冲击腐蚀磨损性能进行了测试。
Under three different impact energy, LCHA with Mn in place of Ni were tested with a modified MLD-10 wear tester to investigate their behavior of corrosive impact abrasion.
采用浸泡腐蚀试验和腐蚀前后的冲击试验并借助于扫描电镜观察,研究了热强碱介质中高锰钢的腐蚀速率和冲击韧度。
The corrosion weight loss rate and impact toughness of high Mn steel in hot concentrated caustic solution were studied by using immersed corrosion, impact test and SEM.
采用浸泡腐蚀试验和腐蚀前后的冲击试验并借助于扫描电镜观察,研究了热强碱介质中高锰钢的腐蚀速率和冲击韧度。
The corrosion weight loss rate and impact toughness of high Mn steel in hot concentrated caustic solution were studied by using immersed corrosion, impact test and SEM.